| 牌號Grade | 粒度分布PSD/μm | 化學成分Chemical/% | 檢測 頻率 Test Frequency |
制成106環 106 Ring 26.9*14.5*11.0mm |
備注Remark | |
| D50 | C | O | 導磁率Permeability （μi） | |||
| T8L | 4.0-6.0 | ≤0.20 | ≤0.50 | 10kHz | ≥55 | |
| T8L-I | 6.0-10.0 | ≤0.20 | ≤0.50 | 10kHz | ≥75 | |
| T8S | 4.0-6.0 | ≤0.20 | ≤0.50 | 10kHz | 25-28 | |
| T2A | 3.0-6.0 | ≤1.50 | ≤1.50 | 200KHz | 9.0-13.0 | |
| T8A3(201) | 3.0-6.0 | ≤0.30 | ≤0.80 | 200kHz | ≥19 | 1g磁環 10.8*6.0*3.0mm |
| T8A5(201) | 5.0-10.0 | ≤0.30 | ≤0.80 | 200kHz | ≥22 | 1g磁環 10.8*6.0*3.0mm |
| T8SK | 4.0-7.0 | ≤0.30 | ≤0.70 | 100kHz | 21.5-25.5 | 絕緣insulation |
| T8SK-B | 5.0-8.0 | ≤0.30 | ≤0.80 | 100kHz | 23.0-27.0 | 絕緣insulation |
| T8A3 | 3.0-6.0 | ≤0.20 | ≤0.60 | 100kHz | 26.0-29.0 | 絕緣insulation |
| T8A3-6JY | 5.0-8.0 | ≤0.20 | ≤0.70 | 100kHz | 27.0-30.0 | 絕緣insulation |
| T8A5 | 3.0-6.0 | ≤0.20 | ≤0.90 | 200kHz | 24.0-29.0 | 絕緣insulation |
| T6A | 1.0-3.0 | ≤1.30 | ≤1.50 | 200kHz | 9.0-11.0 | |
| FeSiCr(-500) | 9.0-13.0 | ≤0.20 | ≤0.65 | 200kHZ | 29-31 | coating |
| FeSiCr(-500)-A | 9-11 | ≤0.20 | ≤0.65 | 200kHz | 27-30 | coating |
| FeSiCr(-500)-B | 10-14 | ≤0.20 | ≤0.80 | 200kHz | 28-31 | coating |
| FeSiCr(-500)-C | 12-17 | ≤0.20 | ≤0.65 | 200kHz | ≥30.5 | coating |
| FeSiCr(-325) | 16.0-20.0 | ＜0.20 | ＜0.60 | 200kHZ | 31-34 | coating |
金屬軟磁粉芯是以金屬軟磁粉末為原料，經絕緣包覆處理后，通過粉末冶金工藝制備而成，具有磁電轉換和儲...
公司現有有效的授權發明專利7項，實用新型專利9項，國際PCT申請專利1項，申請發明專利5項。
9月17-19日，我司參加了在北京國家會議中心舉辦的WorldPM2018 congress。在會展中心取得傲人成績，完成...
2018年12月28日上午，第十二屆全國人大常委、中國科學技術協會原副主席、中南大學原校長、中國工程院院...